Pp Filter Bags Pp Filter Bags manufacture by COX Filter Cloth.
| Locul de origine: | China (Mainland) | Nume de marcă: | OEM | Număr de model: | PP |
| Tip: | Pocket Filter | Materialul sacului: | PP |
Quality Pp Filter Bags supplier by China COX Filter Cloth.
| Pret FOB: | US $1 – 3 / Piece |
| Min.Order Quantity: | 50 Piece/Pieces |
| Capacitate de aprovizionare: | 5000 Piece/Pieces per Month |
| Port: | Shanghai/Shenzhen |
| Condiții de plată: | T/T,Western Union, |
| Detaliu de ambalare: | inner plastic film ,outer carton |
| Detalii de livrare: | 20 working days after deposit |
COX Filter Cloth is one manufacturer of Pp Filter Bags in China.
PP filter bags
corrasion resistance
high quality.anti-abrasion.anti-acid,anti-alkali and lower soften point of PP are be
PP filter bags
corrasion resistance
high quality
anti-abrasion
anti-acid,anti-alkali and lower soften point of PP are better than polyester, and its stability of water solution is excellent, so PP needle punched filter felt is often used in the field is fume temperature under 100°C, the density of acid and alkali is high or the field of filtering solid from liquid that the density of acid and alkali is high.specifiaction:
| Comosition | PP/PP ordinary scrim | PP/PP high strength scrim | ||
| Weight(g/m2) | 500 | 550 | 650 | |
| Thickness(mm) | 2.1 | 2.3 | 2.5 | |
| Air permeability(m3/m2/min) | 12.6 | 10.8 | 8.4 | |
| (N/5×20cm)Tensile strength | Warp | >960 | >1200 | >1500 |
| Weft | >1060 | >1500 | >1800 | |
| Tensile elongation | Warp | <35 | <35 | <35 |
| Weft | <55 | <55 | <55 | |
| Broken strengty (Mpa/min | 2.15 | 2.10 | 2.10 | |
| Working temperature(°C) | ≤88 | ≤88 | ≤88 | |
| Short working temperature(°C) | 110 | 110 | 110 | |
| Anti-acid | Excelent | Excelent | Excelent | |
| Anti-alkali | Excelent | Excelent | Excelent | |
| Anti-abrasion | Excelent | Excelent | Excelent | |
| The stabilityof water solution | Excelent | Excelent | Excelent | |
| Finishing treatment | Singeing or high temperature press | High temperature press on both sides | ||